    Products > Alloy tool steel > > Cr12/1.2080/D3/SKD1
    Product name : Cr12/1.2080/D3/SKD1
    Item : 2014517162244
     Enlarge Image                   Back
    ←[Previous Product]              [Next Product]→


      Details:

    Packaging & Delivery

    Packaging Detail: 20ft: GW:17.5T; (5.80mX2.13mX2.18m,) 40ft: GW:22T; (11.8mX2.13mX2.18m,)
    Delivery Detail: 7 days after the order is exactly confirmed

    Specifications

    Round bar D3 steel 
    1.EAF/ESR provide 
    2.Sample free 
    3.Black or Bright 
    4.T: 25-200mm W:50-610mm L:2000-4000mm

     
    Product Description

    Round bar D3 steel 

    1.Specifications of d3 steel:

     

               Round bar

    Diameter(mm)

    Length (mm)

     

    10~410

    3000~5800

     

     

                    Plate

    Thickness(mm)  

    Width (mm)       

    Length (mm)    

    Max:25-200mm

    50-610mm

    2000~4000 

    The size can be customed!

    2.Equivalent grade:

    AISI/ASTM

    GB

    DIN

    JIS

    BS EN ISO

    D3

    Cr12

    1.208

    SKD1

    X210Cr12

    3.Chemical composition(%) of d3 steel: 

    C

    Si

    Mn

    Cr

    S

    P

    2.00-2.30

    ≤0.40

    ≤0.40

    11.50-13.00

    ≤0.03

    ≤0.03

    4.Heat treatment:

    Isothermal annealing:

    - Heat to 850°Chold for 1/2 hour to 1 hour;

    - Furnace cooling to 770°C and hold at temperature for at least 10 hours;

    -Cool by 10°C /h to 720°C;

    -Cooling in air.

    Stress relieving:

       To be carried out after machining and before the final heat treatment.

    -Heat to 650-700°C, hold for 4/6 hours:

    -Furnace cooling to 330-350°C;

    -Cooling in air.

    Hardening:

    -Initial preheating to 350-450°C;

    -Second preheating to 750-850°Cin salt bath at 850°C;

    -Austenitizing at 960-100°C;

    -Cooling in fluid oil.

    Tempering hardness: 64-65 HRC

    5.Application:

    1.Steel with wear resistance and fairly good dimensional stability during heat treatment. 

    2.Rolls for cold strip mills and wire squeezer mills, circular knives and shear blades.

    3.Dies for small metal parts, punches and drawing dies, dies for sintering, forming tool rollers, shear blades.

    4.Molds for plastic materials. Statically and dynamically stressed components for vehicles,engines and

     machines.

    5.For parts of larger cross-sections,crankshafts,gears,wear-resisting press tool and guide palte.ect.

    6.Characteristic:

    1.Very high resistance against abrasive and adhesive wear due to a high volume of hard carbidesin the steel.

    2.Matrix moderate machinability good dimensional stability

    3.Toughness and through hardenability 

    7.Machinability

    The machinability rating of D3 is roughly 25 % that of free machining carbon steel 1018. 

    Due to its abrasion resistant nature, machining in the hardened condition should be limited to finish grinding.

    8.Inspection:

    100% Ultrasonic according to the test standards:SEP1921-84,GR.3 CLASS C/C or by SGS ,AHK or Alex Stewart

      Related Products :

    AISI O1/ DIN1.2510/ 9CrWMn
    AISI O1/ DIN1.2510/ 9CrWMn

    H13/1.2344/SKD61/4Cr5MoSiV1
    H13/1.2344/SKD61/4Cr5MoSiV1

    Cr12MoV
    Cr12MoV

    small size rolled flat
    small size rolled flat

    peeled forged round
    peeled forged round
    Price: DIA 70-410mm

    O2/1.2842/9Mn2V
    O2/1.2842/9Mn2V

    D2/1.2379/SKD11/Cr12Mo1V1
    D2/1.2379/SKD11/Cr12Mo1V1

    rolled round 10-65mm
    rolled round 10-65mm
    男人的天堂在线